Pu Shoe Upper Resin

Tlhaloso e Khutšoanyane:

Ho Kopanya Mocheso 30℃40℃, Phepo ea Mocheso 80℃90℃, Nako ea Demould 8~10 min (e ka fetoloang), Ho thatafala ha sehlahisoa se felileng ho ka fetoloa ka ho fetola tekanyo ea thepa ea motsoako A+C/B.


Lintlha tsa Sehlahisoa

Li-tag tsa Sehlahisoa

Pu Shoe Upper Resin

MOTSAMAI

Sistimi ena e na le likarolo tse 'ne, polyol, ISO, moemeli oa pheko le catalyst.

LITŠOANTŠISO

Ho Kopanya Mocheso 30℃40℃, Phepo ea Mocheso 80℃90℃, Nako ea Demould 8~10 min (e ka fetoloang), Ho thatafala ha sehlahisoa se felileng ho ka fetoloa ka ho fetola tekanyo ea thepa ea motsoako A+C/B.

POLOKO

Boloka sebakeng se phodileng le se omileng.Haeba u sa khone ho sebelisa moqomo o le mong ka nako e le 'ngoe, ka kopo tlatsa khase ea Nitrogen 'me u koale moropa oo hantle.Nako ea ho paka ea pele ke likhoeli tse 6.

LITŠOANTŠISO MONATE

Mekhahlelo ea ho itšoara

Sehlahisoa se Felletseng ka thata / Lebōpo A

70

74

79

82

Karolelano ea boima

DX3520-B

62

68

75

80

DX3580-A

97

96

95

94

DX3580-C

3

4

5

6

Catalyst / DX3580-A (%)

0.29

0.27

0.25

0.25

Defoaming agent / DX3580-A (%)

0.45

0.47

0.49

0.53

Nako ea gel / min

3

3

3

3

Mechanical Properties ea sehlahisoa se felileng

Thata / Lebopo A

70

74

79

82

Matla a teteaneng / MPa

35

44

47

49

100% Modulus / MPa

2.2

2.8

3.9

5.4

300% Modulus / MPa

4.6

6.5

8.5

9.8

Ultimate Elongation / %

540

520

500

490

Matla a Kgapha

(ntle le Nick) / (KN/m)

56

66

76

89

Matla a Kgapha

(le Nick) / (KN/m)

12

17

22

35