Pu Mold Resin

Tlhaloso e Khutšoanyane:

E na le thepa e babatsehang ea ho sebetsa, nako e khutšoanyane ea gel, e tiileng mocheso o tloaelehileng.Sehlahisoa se phethiloeng se na le thepa e ntle ea ho hanyetsa abrasion, anti-hydrolyzing, pepeneneng, ho ba le botsitso bo botle le tekanyo e tsitsitseng.


Lintlha tsa Sehlahisoa

Li-tag tsa Sehlahisoa

Pu Mold Resin

MOTSAMAI

E na le karolo ea A&B, A ke polyol, 'me B ke Iso-terinated polyurethane prepolymer.

LITŠOANTŠISO

E na le thepa e babatsehang ea ho sebetsa, nako e khutšoanyane ea gel, e tiileng mocheso o tloaelehileng.Sehlahisoa se phethiloeng se na le thepa e ntle ea ho hanyetsa abrasion, anti-hydrolyzing, pepeneneng, ho ba le botsitso bo botle le tekanyo e tsitsitseng.

KOPO

E sebedisetsoa ho etsa lieta le mefuta e fapaneng ea hlobo ea PU.Sebaka sa rabara ea Silicon ho etsa hlobo ea lejoe la setso.

POLOKO

Boloka sebakeng se phodileng le se omileng.Haeba u sa khone ho sebelisa moqomo o le mong ka nako e le 'ngoe, ka kopo tlatsa khase ea Nitrogen 'me u koale moropa oo hantle.Nako ea ho paka ea pele ke likhoeli tse 6.

LITŠOANTŠISO MONATE

B

Mofuta DM1295-B
Ponahalo Seedi se senang mmala kapa se serolwana se bonaletsang
Viscosity (30℃) mPa·s/ 1500±150

A

Mofuta DM1260-A DM1270-A DM1280-A DM1290-A
Ponahalo Mokelikeli o mosehla o kganyang
Viscosity (30℃)/mPa·s 560±200 650±100 750±100 850±100
Karolelano A: B (karolelano ea boima) 1.4:1 1.2:1 1:1 0.7:1
Mocheso oa tšebetso/℃ 25-40
Nako ea gel (30℃)*/min 6 - 15 (e fetohang)
Ponahalo Mokelikeli o mosehla o kganyang
Hardness (lebōpo la A) 60±2 70±2 80±2 90±2
Matla a ho tsieleha/MPa 6 8 10 12
Elongation nakong ea khefu/% 500 ~ 700
Matla a ho tabola/(kN/m) 25 30 40 40
Rebound/ % 60 55 50 48
Matla a khoheli (25℃) (g/cm3 1.07 1.08 1.10

1.11