ʻO ke kāpili polyurethane
Maikaʻi kaʻina hana, hiki ke hoola ma ka lumi wela, pōkole demoulding manawa, a me ka waihoʻoluʻu hiki ke hoʻohui i ke kala.ʻO ka lāʻau i hoʻopau ʻia he kūpaʻa maikaʻi ke kāʻei ʻana, ke kūpaʻa wai, ke aniani, ka elasticity maikaʻi a me ka nui paʻa.
Hiki ke hoʻololi i ka hoʻoheheʻe ʻana i ka lāʻau "pohaku moʻomeheu".Hiki ke hoʻohana ʻia no ka ipuhao mea uila, ka ʻōpala ʻōpala, ka pā pāpaʻi, ka huila kaʻa a me ka mold kāmaʻa a me nā huahana ʻē aʻe.
Mea B | kumu hoʻohālike | DM1295-B | |||
helehelena | ʻAʻole waihoʻoluʻu i ka wai aniani ʻeleʻele | ||||
viscosity(30℃)mPa·s/ | 1500±150 | ||||
Mahele A | kumu hoʻohālike | DM1260-A | DM1270-A | DM1280-A | DM1290-A |
helehelena | Wai melemele māmā | ||||
(30℃)/mPa·s | 560±200 | 650±100 | 750±100 | 850±100 | |
Lakiō A:B(ʻoi) | 1.4:1 | 1.2:1 | 1:1 | 0.7:1 | |
Ka wela hana / ℃ | 25~40 | ||||
Ka manawa gel (30 ℃)*/min | 6~15(Hoʻololi) | ||||
helehelena | Elastomer melemele māmā | ||||
Paʻakiki(ke kahakai A) | 60±2 | 70±2 | 80±2 | 90±2 | |
ikaika uʻi /MPa | 6 | 8 | 10 | 12 | |
Elongation / % | 500~700 | ||||
waimaka ikaika /(kN/m) | 25 | 30 | 40 | 40 | |
Hoʻihoʻi hou / % | 60 | 55 | 50 | 48 | |
Māmā/(g/cm3) | 1.07 | 1.08 | 1.10 | 1.11 |