I-Pu Shoe Upper Resin

Incazelo emfushane:

Ukuxuba Izinga Lokushisa 30℃ 40℃, Izinga Lokushisa Lokuphilisayo 80℃90℃, Isikhathi sokubunjwa 8~10 amaminithi (okulungiswayo), Ukuqina komkhiqizo oqediwe kungalungiswa ngokushintsha isilinganiso sezinto zengxenye A+C/B.


Imininingwane Yomkhiqizo

Omaka bomkhiqizo

I-Pu Shoe Upper Resin

COMPOSITION

Lolu hlelo luqukethe izingxenye ezine, i-polyol, i-ISO, i-ejenti yokwelapha kanye ne-catalyst.

IZIPHUMA

Ukuxuba Izinga Lokushisa 30℃ 40℃, Izinga Lokushisa Lokuphilisayo 80℃90℃, Isikhathi sokubunjwa 8~10 amaminithi (okulungiswayo), Ukuqina komkhiqizo oqediwe kungalungiswa ngokushintsha isilinganiso sezinto zengxenye A+C/B.

ISITOREJI

Gcina endaweni epholile neyomile.Uma ungeke ukwazi ukusebenzisa isigubhu esisodwa ngesikhathi esisodwa, sicela ugcwalise igesi ye-Nitrogen bese uvala isigubhu kahle.Isikhathi seshelufu sokupakisha kwangempela yizinyanga eziyisi-6.

IZIMPAHLA ZOMZIMBA

Amapharamitha wokusabela

Ukuqina Komkhiqizo Ophelile / Ugu A

70

74

79

82

Isilinganiso sobuningi

I-DX3520-B

62

68

75

80

I-DX3580-A

97

96

95

94

I-DX3580-C

3

4

5

6

I-Catalyst / DX3580-A (%)

0.29

0.27

0.25

0.25

I-ejenti yokukhipha amagwebu / DX3580-A (%)

0.45

0.47

0.49

0.53

Isikhathi se-gel / min

3

3

3

3

I-Mechanical Properties yomkhiqizo oqediwe

Ukuqina / Ugu A

70

74

79

82

Amandla okuqina / MPa

35

44

47

49

100% Modulus / MPa

2.2

2.8

3.9

5.4

300% Modulus / MPa

4.6

6.5

8.5

9.8

Ukwelulwa Okukhulu / %

540

520

500

490

Izinyembezi Amandla

(ngaphandle kuka-Nick) / (KN/m)

56

66

76

89

Izinyembezi Amandla

(no-Nick) / (KN/m)

12

17

22

35