Pu Shoe Upper Resin

Inkcazelo emfutshane:

Ukuxuba Ubushushu 30℃ 40℃, Ubushushu boNyango 80~90℃, Ixesha lokumisa 8~10 min (enokulungiswa), Ubulukhuni bemveliso egqityiweyo bunokulungelelaniswa ngokutshintsha umlinganiselo wemathiriyeli wecandelo A+C/B.


Iinkcukacha zeMveliso

Iithegi zeMveliso

Pu Shoe Upper Resin

UHLELO

Le nkqubo inamacandelo amane, i-polyol, i-ISO, i-arhente yokunyanga kunye ne-catalyst.

IIMPAWU

Ukuxuba Ubushushu 30℃ 40℃, Ubushushu boNyango 80~90℃, Ixesha lokumisa 8~10 min (enokulungiswa), Ubulukhuni bemveliso egqityiweyo bunokulungelelaniswa ngokutshintsha umlinganiselo wemathiriyeli wecandelo A+C/B.

UKUGCINA

Gcina kwindawo epholileyo neyomileyo.Ukuba awukwazi ukusebenzisa igubu elinye phezulu ngexesha elinye, nceda ugcwalise igesi yeNitrojeni kwaye ulitywine kakuhle igubu.Ubomi beshelufu yokupakishwa kokuqala ziinyanga ezi-6.

IIPROPATI ZOMZIMBA

Iiparamitha zokusabela

Ukuqina kweMveliso egqityiweyo / Unxweme A

70

74

79

82

Umlinganiselo wobuninzi

DX3520-B

62

68

75

80

DX3580-A

97

96

95

94

DX3580-C

3

4

5

6

I-Catalyst / DX3580-A (%)

0.29

0.27

0.25

0.25

Iarhente yokukhupha ugwebu / DX3580-A (%)

0.45

0.47

0.49

0.53

Ixesha leGel / min

3

3

3

3

IiPropati zeMechanical zemveliso egqityiweyo

Ukuqina / Unxweme A

70

74

79

82

Amandla okuqina / MPa

35

44

47

49

100% Modulus / MPa

2.2

2.8

3.9

5.4

300% Modulus / MPa

4.6

6.5

8.5

9.8

Ubude obugqibeleleyo / %

540

520

500

490

Iinyembezi Amandla

(ngaphandle kukaNick) / (KN/m)

56

66

76

89

Iinyembezi Amandla

(noNick) / (KN/m)

12

17

22

35