I-MDI PRORNEMER
Ubunzima: Shore A5A-Shore A 95A
Imveliso ineempawu zokunganyangeki kakuhle, ukomelela kunye neepropathi ezigqwesileyo.
Isetyenziselwa ukwenza iimveliso ze-Polyctrament Polytorthane ezifana neevili zerabha, iipleyiti zokutywina kunye namakhonkco etywina.
|
Imodeli
| D2560 | D2575 | D2590 | D3565 | D3575 | D3590 |
| I-NCO /% | 6.0 ± 0.2 | 7.5 ± 0.2 | 9.0 ± 0.2 | 6.5 ± 0.2 | 7.5 ± 0.2 | 9.0 ± 0.2 |
| I-State kwi-20 ℃ | Inkqubo ye-PTMG, i-White Short | Inkqubo yePolyester, i-White eqinileyo | ||||
| I-bdoI-100G Replymer / g | 6.1 | 7.8 | 9.3 | 6.8 | 7.8 | 9.3 |
| I-Viskosity (85 ℃) / i-MPAF | I-1400 | I-1000 | I-750 | I-1400 | 1200 | I-1000 |
| Ukuxuba iqondo lobushushu / ℃ (prepolymer / i-1,4bD) | I-80/40 | I-80/40 | I-80/40 | I-80/40 | I-80/40 | I-80/40 |
| Ixesha le-Gel / imiz | 10 | 8 | 7 | 10 | 8 | 7 |
| Ixesha lokuziqhelanisa ne-positication (110 ℃) / h | 48 | 48 | 48 | 48 | 48 | 48 |
| Ubunzima (Shore A) | I-87 ± 2 | I-90 ± 2 | I-95 ± 2 | I-85 ± 2 | I-90 ± 2 | I-95 ± 2 |
| I-100% i-modyul / MPA | 6 | 9.2 | 12.6 | 5 | 8.6 | 12.3 |
| I-300% imodyuli / mpa | 17 | 16.6 | 18.9 | 10 | 19.7 | 29.1 |
| Amandla amanxuwa / i-MPA | 44 | 43 | 45 | 50 | 46 | 55 |
| I-Elong /% | 472 | I-683 | I-500 | I-540 | I-580 | I-530 |
| Amandla e-Tear / (KN / M) | 75 | I-110 | I-130 | 82 | 117 | 132 |
| Rebound /% | 61 | 64 | 55 | 43 | 35 | 39 |
| Ukuxinana (24 ℃) / (g / cm3) | 1.11 | 1.11 | 1.12 | 1.23 | 1.26 | 1.24 |
| I-Din Hick / MM³ | 36 | 44 | 44 | 32 | 35 | 38 |