Polyether / TDI genus prepolymer

Description:


  • MALITIA Price:US $0.5 - 9,999 / Piece
  • Min.Order Quantitas:100 Piece/Picies
  • Facultates copia:(X) Piece / Mass per mense
  • civitas originis:China
  • tincidunt:INOV
  • Product Detail

    Product Tags

    Producta habent bonam gerunt resistentiam, aquae resistentiam, resistentiam fingunt, proprietates mechanicas excellentes, et color colori adici potest accommodare.Solet facere fructus polyurethanos ut Flexilis baculum, rota Flexilis, lamina, Flexilis vestiens et partes miscellaneae.

    Exemplar

    D1140

    D1145

    D1155

    D1160

    D1180

    D1185

    NCO/%

    4.0±0.2

    4.5±0.2

    5.5±0.2

    6.0±0.2

    8.0±0.2

    8.5±0.2

    Publica ad XX

    Hyalina Transparens Liquid

    MOCA100g Prepolymer / g *

    11.5

    13.0

    16.0

    17.5

    23

    24.0

    Viscositas (85℃)/mPa·s

    340

    300

    250

    250

    450

    400

    Mixtio temperatus /℃(Prepolymer/MOCA)

    80/120

    80/120

    80/120

    80/120

    75/110

    75/110

    Gel tempus / min

    10

    9.5

    9

    6

    2

    2

    Post vulcanization tempus (100℃) / h

    10

    10

    10

    10

    10

    10

    Duritiam

    78±2

    82±2

    88±1

    92±1

     

     

    Duritiam. Shore D)

     

     

     

     

    70±1

    78±1

    100% Modulus/MPa

    4.6

    5.0

    5.5

    6.2

    23.2

    32.5

    300% Modulus /MPa

    8.2

    9.2

    13.0

    20.8

    -

    -

    Roboris distrahentes / MPa

    27

    28

    32

    35

    39

    42

    Prolongatio / %

    550

    480

    400

    350

    230

    180

    Robur /(KN/m)

    46

    55

    76

    78

    123

    145

    Resiliant / %

    28

    24

    24

    33

    40

    51

    Densitas (24℃)/(g/cm3)

    1.11

    1.12

    1.14

    1.14

    1.18

    1.18

    Din gerunt /mm³

    148

    112

    109

    141

    131

    89

     

    Exemplar

    D1230

    D1235

    D1240

    D1245

    D1250

    D1262

    D1265

    D1270

    NCO/%

    3.0±0.1

    3.5±0.1

    4.0±0.1

    4.5±0.2

    5.0±0.2

    6.2±0.2

    6.5±0.2

    7.0±0.2

    Publica ad XX

    Hyalina Transparens Liquid

    MOCA

    100g Prepolymer / g *

    8.6

    10.3

    11.5

    13

    14.5

    18

    19

    20.5

    Viscositas (85℃)/mPa·s

    200

    250

    350

    400

    450

    240

    300

    400

    Mixtio temperatus /℃(Prepolymer/MOCA)

    85/120

    85/120

    80/120

    80/120

    80/120

    75/120

    75/120

    75/120

    Gel tempus / min

    9

    5

    4.5

    4

    3.5

    3

    2.5

    2

    Post vulcanization tempus (100℃) / h

    10

    10

    10

    10

    10

    10

    10

    10

    Duritiam

    70±2

    78±2

    84±2

    86±2

    90±1

    94±1

    97±1(53D)

    60D±1

    100% Modulus/MPa

    2.1

    4.2

    5.4

    5.9

    8.9

    9.2

    15.2

    15.8

    300% Modulus /MPa

    3.0

    6.3

    10.0

    10.3

    14.6

    16.8

    24.6

    23

    Roboris distrahentes / MPa

    7

    10

    19

    21

    31

    32

    35

    33

    Prolongatio / %

    600

    550

    500

    480

    460

    450

    440

    420

    Robur /(KN/m)

    34

    44

    53

    57

    73

    78

    95

    120

    Resiliant / %

    50

    48

    41

    31

    30

    31

    41

    43

    Densitas (24℃)/(g/cm3)

    1.08

    1.09

    1.11

    1.13

    1.14

    1.15

    1.16

    1.17

    Din gerunt /mm³

    163

    159

    116

    157

    135

    117

    143

    135.6