Mdi prepolymer
Durness: Litus a 75a - litus a 95a
Quod productum habet proprietates boni gerunt resistentia, mollitiam et excellentior mechanica proprietatibus.
Usus est pro faciens Miscellaneous Polyurethane Elastomer products ut Flexilis rotae, cribrum laminas et signantes annulos.
|
Exemplar
| D2560 | D2575 | D2590 | D3565 | D3575 | D3590 |
| NCO /% | 6.0 ± 0.2 | 7.5 ± 0.2 | 9.0 ± 0.2 | 6,5 ± 0.2 | 7.5 ± 0.2 | 9.0 ± 0.2 |
| State ad XX ℃ | PTMG Ratio, Alba Solidae | Polyester ratio, albus solidum | ||||
| Bdo100g Prepolymer / G | 6,1 | 7,8 | 9,3 | 6,8 | 7,8 | 9,3 |
| Viscosity (LXXXV ℃) / mpa · s | MCD | M | DCCL | MCD | MCC | M |
| Mixing Temperature / ℃ (Prepolymer / 1,4BD) | 80/40 | 80/40 | 80/40 | 80/40 | 80/40 | 80/40 |
| Gel tempus / min | 10 | 8 | 7 | 10 | 8 | 7 |
| Post Vulcanization Tempus (CX ℃) / h | 48 | 48 | 48 | 48 | 48 | 48 |
| Durness (litus a) | LXXXVII ± II | XC ± II | XCV ± II | LXXXV ± II | XC ± II | XCV ± II |
| C% modulus / MPA | 6 | 9,2 | 12,6 | 5 | 8,6 | 12.3 |
| CCC% modulus / MPA | 17 | 16.6 | 18.9 | 10 | 19,7 | 29.1 |
| Tensile fortitudo / MPA | 44 | 43 | 45 | 50 | 46 | 55 |
| Elongatio /% | CDLXXII | DCLXXXIII | D | DXL | DLXXX | DXXX |
| PRAETEMPTO viribus / (K / M) | 75 | CX | CXXX | 82 | CXVII | CXXXII |
| Rebound /% | 61 | 64 | 55 | 43 | 35 | 39 |
| Density (XXIV ℃) / (G / cm3) | 1,11 | 1,11 | 1.12 | 1.23 | 1.26 | 1.24 |
| Laudate gerunt / mm³ | 36 | 44 | 44 | 32 | 35 | 38 |