Polycaprolactone type prepolymer
Paʻakiki； kahakai A 60A – kahakai A 95A
Loaʻa i ka huahana nā hiʻohiʻona o ka operability maikaʻi, ākea ākea ākea, maikaʻi
| Hoʻohālike | D4336 | D4142 | D4152 | D4160 |
| NCO/% | 3.6±0.2 | 4.2±0.2 | 5.2±0.2 | 6.0±0.2 |
| Kūlana ma 20 ℃ | Paʻa melemele māmā | |||
| MOCA100g Prepolymer / g | 10.5 | 12 | 14.9 | 17.5 |
| Ka wela hui ʻana / ℃（ Prepolymer / MOCA） | 80/120 | 80/120 | 80/120 | 80/120 |
| Ka manawa gel / min | 8 | 8 | 7.5 | 4 |
| ʻO ka manawa ma hope o ka vulcanization (100 ℃) /h | 16 | 16 | 16 | 16 |
| ʻOʻoleʻa（Kai A） | 80±2 | 88±2 | 92±2 | 94±2 |
| 100% Modulus/MPa | 3.3 | 5.4 | 7.3 | 10.5 |
| 300% Modulus /MPa | 6.1 | 10.6 | 15.6 | 18.7 |
| Ka ikaika uʻi /MPa | 45 | 45 | 50 | 52 |
| Elongation / % | 550 | 520 | 480 | 450 |
| Kaha waimaka /（KN/m） | 51 | 76 | 99 | 110 |