I-Pu Famis Shoe Sole System
I-Pu Famis Shoe Sole System
IUkunqunyelwa
Uhlelo lwe-Pu Famis Shoe-Sole lusetshenziselwa ukwenza ama-soe shoe shoe kanye nama-soles angaphakathi. Yinto e-polyester-based pu yohlelo lwe-polyester, iqukethe izakhi ezine, i-polylol, iso, i-hardiner ne-catalyst. Ukucutshungulwa kohlelo kuyizakhi ezimbili. I-Catalyst, enzima, i-ejenti evuthayo kanye ne-pigment kufanele ihlanganiswe kahle ne-polyol compol exd-3270a, bese uxuba nengxenye ye-iso exd-3119b yokwenza izimpahla zokugcina.
Izakhiwo Ezibonakalayo
A, i-iNNENer Soles yendlela yokupheka yezicathulo zokuphepha:
| Into | Exd-3270a | Exd-311bb |
| Isilinganiso (isilinganiso sesisindo) | 100 | 85 ~ 88 |
| Izinga lokushisa lezinto ezibonakalayo (℃) | 45 ~ 50 | 45 ~ 50 |
| Isikhathi (s) | 5 ~ 7 | |
| Isikhathi samahhala (s) | 30 ~ 50 | |
| Mahhala Foam density (G / cm3Isihlehlukene | 0.35 ~ 0.4 | |
| Izinga lokushisa le-Main (℃) | 45 ~ 55 | |
| Ubuningi bomkhiqizo (G / cm3Isihlehlukene | 0.5 ~ 0.55 | |
| Ubulukhuni (ogwini a) | 55 ~ 65 | |
| Isikhathi esidala (min) | 3 | |
| Ukunwebeka ngekhefu (%) | ≥550 | |
| Amandla ezinyathelani (KN / M) | ≥22 | |
| Amandla we-Tensile (MPA) | ≥6.0 | |
| I-Ross flexing Ukushisa kwegumbi | Izikhathi ezingama-50 000 akukho ukuqhekeka | |
B, I-OutoLe Yendlela Yokuphepha Izicucu-Zokulunga Indlela Yokulungisa:
| Into | Exd-3270a | Exd-311bb |
| Isilinganiso (isilinganiso sesisindo) | 100 | 82 ~ 85 |
| Izinga lokushisa lezinto ezibonakalayo (℃) | 45 ~ 50 | 45 ~ 50 |
| Isikhathi (s) | 5 ~ 7 | |
| Isikhathi samahhala (s) | 30 ~ 50 | |
| Mahhala Foam density (G / cm3Isihlehlukene | 0.55 ~ 0.6 | |
| Izinga lokushisa le-Main (℃) | 45 ~ 55 | |
| Ubuningi bomkhiqizo (G / cm3Isihlehlukene | 0.6 ~ 0.8 | |
| Ubulukhuni (ogwini a) | 65 ~ 75 | |
| Isikhathi esidala (min) | 3 | |
| Ukunwebeka ngekhefu (%) | ≥600 | |
| Amandla ezinyathelani (KN / M) | ≥28 | |
| Amandla we-Tensile (MPA) | ≥7.3 | |
| Izinga lokushisa legumbi le-ross | Izikhathi ezingama-50 000 akukho ukuqhekeka | |
| Isikhathi esidala (min) | 3 | |
| Ubuningi bomkhiqizo (G / cm3) | 0.2 ~ 0.3 | |
| Ubulukhuni (ogwini c) | 30 ~ 40 | |
| Amandla we-Tensile (MPA) | 0.45-0.50 | |
| Amandla ezinyathelani (KN / M) | I-2.50-2.60 | |
| I-Elongation (%) | 280-300 | |