Donfoam 813 CP/IP base blend polyols for block Foam
Donfoam 813 CP/IP base blend polyols for block Foam
ISINGENISO
I-Donfoam813 blend polyols zisebenzisa i-CP noma i-CP/IP njenge-ejenti efuthayo, esetshenziswa ekukhiqizeni igwebu le-PIR elibushelelezi ilangabi eliphezulu, elisebenza nge-foam cell cell, ukuguquguquka okuphansi kwe-thermal, ukwahlukanisa okuhle okushisayo kanye ne-flame retardant, izinga lokushisa eliphansi alikho ukuqhekeka okunciphayo njll. Isetshenziswa kabanzi kwinqubo yazo zonke izinhlobo zomsebenzi wokufakelwa okufana nokwakhiwa kodonga lwangaphandle, isitoreji esibandayo, amathangi, amapayipi amakhulu njll.
IMPAHLA YOMNYAMA
| Ukubukeka I-viscosity enamandla (25℃) mPa.S Ukuminyana (20℃) g/ml Izinga lokushisa lesitoreji ℃ Inyanga yokuzinza kwesitoreji | Uketshezi olukhanyayo oluphuzi kuya kokunsundu 500±100 1.20±0.1 10-25 6 |
ISILINGANISO ESINCONYWAYO
| Izinto | I-PBW |
| Hlanganisa ama-Polyols I-CP noma i-CP/IP Isocyanate | 100 11-13 140-150 |
UBUCHWEPHESHE KANYE NE-REACTIVITY(inani eliqondile liyahlukahluka kuye ngezimo zokucubungula)
| Ukuxuba Mathupha | |
| I-Raw Material Temperature ℃ Izinga lokushisa lesikhunta ℃ I-CT s I-GT s I-TFT s Ukuminyana Kwamahhala kg/m3 | 20-25 I-Ambient Temperature (15-45℃) 35-60 140-200 240-360 28-35 |
IMISEBENZI YEgwebu
| Into | Izinga Lokuhlola | Ukucaciswa |
| Ukuminyana Kokubumba Kukonke I-Molding Core Density | I-ASTM D1622 | ≥50kg/m3 ≥40kg/m |
| Isilinganiso Seseli Elivaliwe | I-ASTM D2856 | ≥90% |
| I-Intial Thermal Conductivity (15℃) | I-ASTM C518 | ≤24mW/(mK) |
| Amandla Acindezelayo | I-ASTM D1621 | ≥150kPa |
| Ukuzinza kweDimensional 24h -20℃ RH90 70℃ | I-ASTM D2126 | ≤1% ≤1.5% |
| Izinga Lokumunca Amanzi | I-ASTM D2842 | ≤3% |