PES/TDI jara

Apejuwe kukuru:


  • Iye owo FOB:US $ 0.5 - 9,999 / nkan
  • Min.Oye Ibere:100 nkan / nkan
  • Agbara Ipese:10000 Nkan / Awọn nkan fun oṣu kan
  • ilu isenbale:China
  • aami-iṣowo:INOV
  • Alaye ọja

    ọja Tags

    lile: tera A 60A – tera D 70D

    Awọn ọja ni o ni awọn abuda kan ti o dara operability, jakejado líle ibiti, ti o dara yiya resistance, resilience ati ki o tayọ darí ini.

    Ti a lo fun ṣiṣe awọn ọja elastomer polyurethane oriṣiriṣi gẹgẹbi awọn kẹkẹ rọba, awọn awo sieve, scrapers, awọn oruka edidi ati awọn taya.

     

    Awoṣe

    D3125

    D3136

    D3143

    D3145

    D3160

    D3170

    NCO/%

    2.5± 0.2

    3.6 ± 0.2

    4.3 ± 0.2

    4.5± 0.2

    6.0 ± 0.2

    7.0 ± 0.2

    Ipinle ni 20 ℃

    funfun ri to

    MOCA100g Prepolymer / g

    7.2

    10.5

    12.5

    13.2

    17.2

    20.0

    Iwo (85℃)/mPa·s

    2800

    1800

    1300

    1200

    900

    800

    Adalu otutu / ℃ (Prepolymer / MOCA)

    85/120

    85/120

    80/120

    80/120

    75/120

    75/120

    Jeli akoko / min

    16

    9

    8

    7.5

    5

    4.5

    Akoko vulcanization lẹhin (100 ℃) /h

    10

    10

    10

    10

    10

    10

    Lile (Okun A)

    76±2

    85±2

    92±2

    91±2

    96±2

    97±2

    100% Modulu / MPa

    3.4

    4.2

    6.3

    6.7

    11.5

    18.0

    300% Modulu / MPa

    4.1

    8.3

    11.8

    12.5

    21.3

    35.7

    Agbara fifẹ /MPa

    40

    48

    50

    52

    55

    55

    Ilọsiwaju /%

    700

    670

    630

    610

    530

    410

    Agbara omije / (KN/m)

    55

    75

    105

    95

    124

    152

    Ipadabọ /%

    42

    39

    37

    32

    33

    33

    iwuwo (24℃)/(g/cm3)

    1.25

    1.26

    1.27

    1.27

    1.29

    1.29

    Din wọ / mm³

    33

    40

    48

    53

    57

    56

     

     

     

     

     

     

     

     

    Awoṣe

    D3230

    D3236

    D3243

    D3245

    D3249

    D3260

    NCO/%

    3.0± 0.2

    3.6 ± 0.2

    4.3 ± 0.2

    4.5± 0.2

    4.9 ± 0.2

    6.0 ± 0.2

    Ipinle ni 20 ℃

    funfun ri to

    MOCA

    100g Prepolymer / g

    8.6

    10.5

    12.5

    13

    14.5

    17.5

    Iwo (85℃)/mPa·s

    2500

    2000

    1400

    1300

    900

    1200

    Adalu otutu / ℃ (Prepolymer / MOCA)

    85/120

    80/120

    80/120

    80/120

    75/120

    75/110

    Jeli akoko / min

    5

    4

    4

    3

    3

    2

    Akoko vulcanization lẹhin (100 ℃) /h

    10

    10

    10

    10

    10

    10

    Lile (Okun A)

    80±2

    86

    92±1

    92±1

    94±1

    96(52D)

    100% Modulu / MPa

    4.0

    5.1

    6.1

    6.8

    7.3

    12.2

    300% Modulu / MPa

    6.5

    9.8

    11.4

    12.6

    13.4

    20.9

    Agbara fifẹ /MPa

    45

    49

    48

    49

    50

    58

    Ilọsiwaju /%

    750

    690

    650

    600

    580

    530

    Agbara omije / (KN/m)

    61

    88

    99

    100

    106

    132

    Ipadabọ /%

    38

    44

    37

    38

    41

    41

    iwuwo (24℃)/(g/cm3)

    1.25

    1.26

    1.27

    1.27

    1.27

    1.28

    Din wọ / mm³

    41

    44

    44

    50

    54

    55