Le mveliso luhlobo lokudibanisa polyls ngamanzi njengearhente yokufihla, ephandwe ngokukhethekileyo kwi-Puf i-rigid puf ivelise imibhobho ye-inshurensi. Isetyenziswe ngokubanzi kwimibhobho ye-steam, irhasi yerhasi esebenzayo yerhasi, imibhobho yeoyile kunye namanye amasimi. Iimpawu zezi zilandelayo:
.
(2) Ukunganyangeki kweqondo lobushushu obuphezulu, ukuma ixesha elide kwi-150 ℃
(3) Uzinzo lobushushu obuhle kakhulu
Ipropathi yomzimba
Imbonakalo | Ukukhanya kwetyheli ukuya kulwelo oluBrown |
I-HYDROXYL Ixabiso MGKh / G | I-250-450 |
I-viscosity eguqukayo (25 ℃) ye-MPA.S | I-300-600 |
Ukuxinana (20 ℃) g / ml | 1.10-1.16 |
Iqondo lokugcina ℃ | I-10-25 |
Inyanga yokugcina indawo yokugcina | 6 |
Itekhnoloji kunye nokuHlala.
| Ukudityaniswa kwencwadana | Umatshini oPhakamileyo |
I-ratio (pol / i-iso) | 1: 1.40-1.1.60 | 1: 1.40-1.60 |
Ixesha lokunyuka s | 20-40 | 15-35 |
I-gel yexesha s | 80-200 | 80-160 |
I-Tack Times S | ≥150 | ≥150 |
Ukuxinana simahla kg / m3 | 34.0-36.0 | 33.0-35.0 |
I-Foam Deays
Ukuxinana kobunzi | GB 6343 | I-60-80kg / m3 |
Ixabiso leseli evaliweyo | I-GB 10799 | ≥90% |
Ukuqhutywa kwe-thermal (15 ℃) | I-GB 3399 | ≤33MW / (MK) |
Amandla oxinzelelo | I-GB / T8813 | ≥250kpa |
Ukufunxa kwamanzi | I-GB 8810 | ≤3 (v / v)% |
Ukuzinza kwe-24h -30 ℃ | I-GB / T8811 | ≤1.0% |
24h 100 ℃ | ≤1.5% |