Polima ya aina ya polyether/TDI
Bidhaa hizo zina upinzani mzuri wa kuvaa, upinzani wa maji, upinzani wa mold, mali bora ya mitambo, na rangi inaweza kuongezwa ili kurekebisha rangi.Inatumika kutengeneza bidhaa za polyurethane kama vile fimbo ya mpira, gurudumu la mpira, sahani, mipako ya mpira na sehemu tofauti.
| Mfano | D1140 | D1145 | D1155 | D1160 | D1180 | D1185 |
| NCO/% | 4.0±0.2 | 4.5±0.2 | 5.5±0.2 | 6.0±0.2 | 8.0±0.2 | 8.5±0.2 |
| Hali katika 20 ℃ | Kioevu kisicho na rangi cha Uwazi | |||||
| MOCA100g Prepolymer /g | 11.5 | 13.0 | 16.0 | 17.5 | 23 | 24.0 |
| Mnato (85℃)/mPa·s | 340 | 300 | 250 | 250 | 450 | 400 |
| Kuchanganya halijoto /℃ (Prepolymer/MOCA) | 80/120 | 80/120 | 80/120 | 80/120 | 75/110 | 75/110 |
| Wakati wa gel / min | 10 | 9.5 | 9 | 6 | 2 | 2 |
| Muda wa baada ya kuathiriwa (100℃) /h | 10 | 10 | 10 | 10 | 10 | 10 |
| Ugumu (Pwani A) | 78±2 | 82±2 | 88±1 | 92±1 |
|
|
| Ugumu (Pwani D) |
|
|
|
| 70±1 | 78±1 |
| 100% Modulus/MPa | 4.6 | 5.0 | 5.5 | 6.2 | 23.2 | 32.5 |
| 300% Modulus /MPa | 8.2 | 9.2 | 13.0 | 20.8 | - | - |
| Nguvu ya mkazo/MPa | 27 | 28 | 32 | 35 | 39 | 42 |
| Kurefusha / % | 550 | 480 | 400 | 350 | 230 | 180 |
| Nguvu ya machozi / (KN/m) | 46 | 55 | 76 | 78 | 123 | 145 |
| Kurudi nyuma / % | 28 | 24 | 24 | 33 | 40 | 51 |
| Uzito (24℃)/(g/cm3) | 1.11 | 1.12 | 1.14 | 1.14 | 1.18 | 1.18 |
| Din wear /mm³ | 148 | 112 | 109 | 141 | 131 | 89 |
| Mfano | D1230 | D1235 | D1240 | D1245 | D1250 | D1262 | D1265 | D1270 |
| NCO/% | 3.0±0.1 | 3.5±0.1 | 4.0±0.1 | 4.5±0.2 | 5.0±0.2 | 6.2±0.2 | 6.5±0.2 | 7.0±0.2 |
| Hali katika 20 ℃ | Kioevu kisicho na rangi cha Uwazi | |||||||
| MOCA 100g Prepolymer /g | 8.6 | 10.3 | 11.5 | 13 | 14.5 | 18 | 19 | 20.5 |
| Mnato (85℃)/mPa·s | 200 | 250 | 350 | 400 | 450 | 240 | 300 | 400 |
| Kuchanganya halijoto /℃ (Prepolymer/MOCA) | 85/120 | 85/120 | 80/120 | 80/120 | 80/120 | 75/120 | 75/120 | 75/120 |
| Wakati wa gel / min | 9 | 5 | 4.5 | 4 | 3.5 | 3 | 2.5 | 2 |
| Muda wa baada ya kuathiriwa (100℃) /h | 10 | 10 | 10 | 10 | 10 | 10 | 10 | 10 |
| Ugumu (Pwani A) | 70±2 | 78±2 | 84±2 | 86±2 | 90±1 | 94±1 | 97±1(53D) | 60D±1 |
| 100% Modulus/MPa | 2.1 | 4.2 | 5.4 | 5.9 | 8.9 | 9.2 | 15.2 | 15.8 |
| 300% Modulus /MPa | 3.0 | 6.3 | 10.0 | 10.3 | 14.6 | 16.8 | 24.6 | 23 |
| Nguvu ya mkazo/MPa | 7 | 10 | 19 | 21 | 31 | 32 | 35 | 33 |
| Kurefusha / % | 600 | 550 | 500 | 480 | 460 | 450 | 440 | 420 |
| Nguvu ya machozi / (KN/m) | 34 | 44 | 53 | 57 | 73 | 78 | 95 | 120 |
| Kurudi nyuma / % | 50 | 48 | 41 | 31 | 30 | 31 | 41 | 43 |
| Uzito (24℃)/(g/cm3) | 1.08 | 1.09 | 1.11 | 1.13 | 1.14 | 1.15 | 1.16 | 1.17 |
| Din wear /mm³ | 163 | 159 | 116 | 157 | 135 | 117 | 143 | 135.6 |