Polyether/TDI mofuta oa prepolymer
Lihlahisoa li na le khanyetso e ntle ea ho apara, ho hanyetsa metsi, ho hanyetsa hlobo, thepa e ntle ea mochine, 'me mebala e ka ekeletsoa ho fetola' mala.E sebelisetsoa ho etsa lihlahisoa tsa polyurethane tse kang thupa ea rabara, lebili la rabara, poleiti, ho roala rabara le likarolo tse fapaneng.
| Mohlala | D1140 | D1145 | D1155 | D1160 | D1180 | D1185 |
| NCO/% | 4.0±0.2 | 4.5±0.2 | 5.5±0.2 | 6.0±0.2 | 8.0±0.2 | 8.5±0.2 |
| Boemong ba 20 ℃ | Mokelikeli oa Transparent o senang Mebala | |||||
| MOCA100g Prepolymer /g | 11.5 | 13.0 | 16.0 | 17.5 | 23 | 24.0 |
| Viscosity (85℃)/mPa·s | 340 | 300 | 250 | 250 | 450 | 400 |
| Ho kopanya mocheso / ℃ (Prepolymer/MOCA) | 80/120 | 80/120 | 80/120 | 80/120 | 75/110 | 75/110 |
| Nako ea gel /min | 10 | 9.5 | 9 | 6 | 2 | 2 |
| Nako ea ho senyeha ha poso (100℃) /h | 10 | 10 | 10 | 10 | 10 | 10 |
| Hardness (Shore A) | 78±2 | 82±2 | 88±1 | 92±1 |
|
|
| Hardness (Shore D) |
|
|
|
| 70±1 | 78±1 |
| 100% Modulus/MPa | 4.6 | 5.0 | 5.5 | 6.2 | 23.2 | 32.5 |
| 300% Modulus /MPa | 8.2 | 9.2 | 13.0 | 20.8 | - | - |
| Matla a ho tsieleha /MPa | 27 | 28 | 32 | 35 | 39 | 42 |
| Elongation / % | 550 | 480 | 400 | 350 | 230 | 180 |
| Matla a ho tabola /(KN/m) | 46 | 55 | 76 | 78 | 123 | 145 |
| Rebound / % | 28 | 24 | 24 | 33 | 40 | 51 |
| Density (24℃)/(g/cm3) | 1.11 | 1.12 | 1.14 | 1.14 | 1.18 | 1.18 |
| Din wear/mm³ | 148 | 112 | 109 | 141 | 131 | 89 |
| Mohlala | D1230 | D1235 | D1240 | D1245 | D1250 | D1262 | D1265 | D1270 |
| NCO/% | 3.0±0.1 | 3.5±0.1 | 4.0±0.1 | 4.5±0.2 | 5.0±0.2 | 6.2±0.2 | 6.5±0.2 | 7.0±0.2 |
| Boemong ba 20 ℃ | Mokelikeli oa Transparent o senang Mebala | |||||||
| MOCA 100g Prepolymer /g | 8.6 | 10.3 | 11.5 | 13 | 14.5 | 18 | 19 | 20.5 |
| Viscosity (85℃)/mPa·s | 200 | 250 | 350 | 400 | 450 | 240 | 300 | 400 |
| Ho kopanya mocheso / ℃ (Prepolymer/MOCA) | 85/120 | 85/120 | 80/120 | 80/120 | 80/120 | 75/120 | 75/120 | 75/120 |
| Nako ea gel /min | 9 | 5 | 4.5 | 4 | 3.5 | 3 | 2.5 | 2 |
| Nako ea ho senyeha ha poso (100℃) /h | 10 | 10 | 10 | 10 | 10 | 10 | 10 | 10 |
| Hardness (Shore A) | 70±2 | 78±2 | 84±2 | 86±2 | 90±1 | 94±1 | 97±1 (53D) | 60D±1 |
| 100% Modulus/MPa | 2.1 | 4.2 | 5.4 | 5.9 | 8.9 | 9.2 | 15.2 | 15.8 |
| 300% Modulus /MPa | 3.0 | 6.3 | 10.0 | 10.3 | 14.6 | 16.8 | 24.6 | 23 |
| Matla a ho tsieleha /MPa | 7 | 10 | 19 | 21 | 31 | 32 | 35 | 33 |
| Elongation / % | 600 | 550 | 500 | 480 | 460 | 450 | 440 | 420 |
| Matla a ho tabola /(KN/m) | 34 | 44 | 53 | 57 | 73 | 78 | 95 | 120 |
| Rebound / % | 50 | 48 | 41 | 31 | 30 | 31 | 41 | 43 |
| Density (24℃)/(g/cm3) | 1.08 | 1.09 | 1.11 | 1.13 | 1.14 | 1.15 | 1.16 | 1.17 |
| Din wear/mm³ | 163 | 159 | 116 | 157 | 135 | 117 | 143 | 135.6 |