Pu Shoe Upper Resin

Tsanangudzo Pfupi

Kusanganisa Tembiricha 30~40℃, Kurapa Tembiricha 80℃90℃, Demould nguva 8~10 min (inochinjika), Kuoma kwechigadzirwa chakapedzwa kunogona kugadziriswa nekushandura chiyero chemidziyo yechikamu A+C/B.


Product Detail

Product Tags

Pu Shoe Upper Resin

COMPOSITION

Iyi sisitimu ine zvikamu zvina, polyol, ISO, kurapa agent uye catalyst.

ZVINHU

Kusanganisa Tembiricha 30~40℃, Kurapa Tembiricha 80℃90℃, Demould nguva 8~10 min (inochinjika), Kuoma kwechigadzirwa chakapedzwa kunogona kugadziriswa nekushandura chiyero chemidziyo yechikamu A+C/B.

STORAGE

Chengetedza munzvimbo inotonhorera uye yakaoma.Kana usingakwanise kushandisa dhiramu rimwe chete panguva imwe, ndapota zadza gasi reNitrogen uye uname dhiramu racho zvakanaka.Hupenyu hwesherufu hwekutanga kurongedza ndeye 6 mwedzi.

ZVINHU ZVINHU

Reaction parameters

Yakapedzwa Chigadzirwa Kuoma / Shore A

70

74

79

82

Misa ratio

DX3520-B

62

68

75

80

DX3580-A

97

96

95

94

DX3580-C

3

4

5

6

Catalyst / DX3580-A (%)

0.29

0.27

0.25

0.25

Defoaming agent / DX3580-A (%)

0.45

0.47

0.49

0.53

Gel nguva / min

3

3

3

3

Mechanical Properties yechigadzirwa chakapedzwa

Kuoma / Shore A

70

74

79

82

Tensile simba / MPa

35

44

47

49

100% Modulus / MPa

2.2

2.8

3.9

5.4

300% Modulus / MPa

4.6

6.5

8.5

9.8

Ultimate Elongation / %

540

520

500

490

Tear Strength

(pasina Nick) / (KN/m)

56

66

76

89

Tear Strength

(naNick) / (KN/m)

12

17

22

35