Polyether/TDI mhando prepolymer
Zvigadzirwa zvine kumira zvakanaka kupfeka, kuramba kwemvura, mold kuramba, yakanakisa michina zvivakwa, uye ruvara runogona kuwedzerwa kugadzirisa ruvara.Inoshandiswa kugadzira zvigadzirwa zve polyurethane senge rubber stick, vhiri rerabha, ndiro, rubber coating uye zvakasiyana-siyana.
| Model | D1140 | D1145 | D1155 | D1160 | D1180 | D1185 |
| NCO/% | 4.0±0.2 | 4.5±0.2 | 5.5±0.2 | 6.0±0.2 | 8.0±0.2 | 8.5±0.2 |
| Nyika pa20 ℃ | Colorless Transparent Liquid | |||||
| MOCA100g Prepolymer / g | 11.5 | 13.0 | 16.0 | 17.5 | 23 | 24.0 |
| Viscosity (85℃)/mPa·s | 340 | 300 | 250 | 250 | 450 | 400 |
| Kusanganisa tembiricha / ℃ (Prepolymer/MOCA) | 80/120 | 80/120 | 80/120 | 80/120 | 75/110 | 75/110 |
| Gel nguva / min | 10 | 9.5 | 9 | 6 | 2 | 2 |
| Post vulcanization nguva (100 ℃) / h | 10 | 10 | 10 | 10 | 10 | 10 |
| Kuoma (Shore A) | 78±2 | 82±2 | 88±1 | 92±1 |
|
|
| Kuoma (Shore D) |
|
|
|
| 70±1 | 78±1 |
| 100% Modulus/MPa | 4.6 | 5.0 | 5.5 | 6.2 | 23.2 | 32.5 |
| 300% Modulus / MPa | 8.2 | 9.2 | 13.0 | 20.8 | - | - |
| Tensile simba /MPa | 27 | 28 | 32 | 35 | 39 | 42 |
| Elongation / % | 550 | 480 | 400 | 350 | 230 | 180 |
| Kubvarura simba / (KN/m) | 46 | 55 | 76 | 78 | 123 | 145 |
| Rebound / % | 28 | 24 | 24 | 33 | 40 | 51 |
| Density (24℃)/(g/cm3) | 1.11 | 1.12 | 1.14 | 1.14 | 1.18 | 1.18 |
| Din kupfeka /mm³ | 148 | 112 | 109 | 141 | 131 | 89 |
| Model | D1230 | D1235 | D1240 | D1245 | D1250 | D1262 | D1265 | D1270 |
| NCO/% | 3.0±0.1 | 3.5±0.1 | 4.0±0.1 | 4.5±0.2 | 5.0±0.2 | 6.2±0.2 | 6.5±0.2 | 7.0±0.2 |
| Nyika pa20 ℃ | Colorless Transparent Liquid | |||||||
| MOCA 100g Prepolymer / g | 8.6 | 10.3 | 11.5 | 13 | 14.5 | 18 | 19 | 20.5 |
| Viscosity (85℃)/mPa·s | 200 | 250 | 350 | 400 | 450 | 240 | 300 | 400 |
| Kusanganisa tembiricha / ℃ (Prepolymer/MOCA) | 85/120 | 85/120 | 80/120 | 80/120 | 80/120 | 75/120 | 75/120 | 75/120 |
| Gel nguva / min | 9 | 5 | 4.5 | 4 | 3.5 | 3 | 2.5 | 2 |
| Post vulcanization nguva (100 ℃) / h | 10 | 10 | 10 | 10 | 10 | 10 | 10 | 10 |
| Kuoma (Shore A) | 70±2 | 78±2 | 84±2 | 86±2 | 90±1 | 94±1 | 97±1 (53D) | 60D±1 |
| 100% Modulus/MPa | 2.1 | 4.2 | 5.4 | 5.9 | 8.9 | 9.2 | 15.2 | 15.8 |
| 300% Modulus / MPa | 3.0 | 6.3 | 10.0 | 10.3 | 14.6 | 16.8 | 24.6 | 23 |
| Tensile simba /MPa | 7 | 10 | 19 | 21 | 31 | 32 | 35 | 33 |
| Elongation / % | 600 | 550 | 500 | 480 | 460 | 450 | 440 | 420 |
| Kubvarura simba / (KN/m) | 34 | 44 | 53 | 57 | 73 | 78 | 95 | 120 |
| Rebound / % | 50 | 48 | 41 | 31 | 30 | 31 | 41 | 43 |
| Density (24℃)/(g/cm3) | 1.08 | 1.09 | 1.11 | 1.13 | 1.14 | 1.15 | 1.16 | 1.17 |
| Din kupfeka /mm³ | 163 | 159 | 116 | 157 | 135 | 117 | 143 | 135.6 |