Pu Shoe Upper Resin

Fa'amatalaga Puupuu:

Faʻafefiloi vevela 30 ~ 40 ℃, Curing Temperature 80 ~ 90 ℃, Demould taimi 8 ~ 10 min (fetuunaʻi), le Maaa o oloa maeʻa e mafai ona fetuunai e ala i le suia o le fua faatatau o mea A + C / B.


Fa'amatalaga Oloa

Faailoga o oloa

Pu Shoe Upper Resin

FA'AVAE

O lenei faiga e aofia ai vaega e fa, polyol, ISO, curing agent ma catalyst.

UIGA

Faʻafefiloi vevela 30 ~ 40 ℃, Curing Temperature 80 ~ 90 ℃, Demould taimi 8 ~ 10 min (fetuunaʻi), le Maaa o oloa maeʻa e mafai ona fetuunai e ala i le suia o le fua faatatau o mea A + C / B.

TEU

Teu i se nofoaga malulu ma mago.Afai e le mafai ona e fa'aogaina le pa'u e tasi i le taimi e tasi, fa'amolemole fa'atumu le kasa Nitrogen ma fa'amau lelei le pa'u.O le fa'agata o le fa'aputu muamua e 6 masina.

METOTIA FAALETINO

Fa'atatauga tali

Ma'a'a Oloa Ma'ea/Tagata A

70

74

79

82

Mass ratio

DX3520-B

62

68

75

80

DX3580-A

97

96

95

94

DX3580-C

3

4

5

6

Catalyst / DX3580-A(%)

0.29

0.27

0.25

0.25

Su'i fa'a'ofuofu / DX3580-A(%)

0.45

0.47

0.49

0.53

Gel taimi / min

3

3

3

3

Meatotino Fa'ainisinia o oloa mae'a

Ma'a'a/A'ai A

70

74

79

82

Malosi fa'amalosi / MPa

35

44

47

49

100% Modulus / MPa

2.2

2.8

3.9

5.4

300% Modulus / MPa

4.6

6.5

8.5

9.8

Fa'a'umi'umi Sili /%

540

520

500

490

Malosi Loimata

(e aunoa ma Nick) / (KN/m)

56

66

76

89

Malosi Loimata

(ma Nick ) / (KN/m)

12

17

22

35