Donfoam 813 CP/IP Base Blend Poliols za blok pjenu
Donfoam 813 CP/IP Base Blend Poliols za blok pjenu
UVOD
Donfoam813 blend polyols use CP or CP/IP as blowing agent ,used in the production of high flame retardant PIR block foam, with performances of uniform foam cell , low thermal conductivity, good thermal insulation and flame retardant, low temperature no shrinking crack etc. Widely used in the process of all kinds of insulation work such as: building external wall, cold storage, tanks, large pipes etc.
Fizičko vlasništvo
| Izgled Dinamička viskoznost （25 ℃） MPA.S Gustoća （20 ℃） g/ml Temperatura skladištenja ℃ Mjesec stabilnosti skladištenja | Svijetlo žuta do smeđa prozirna tekućina 500 ± 100 1,20 ± 0,1 10-25 6 |
Preporučeni omjer
| Predmeti | PBW |
| Miješaju polioli CP ili CP/IP Izocijanat | 100 11-13 140-150 |
Tehnologija i reaktivnost(Točna vrijednost varira ovisno o uvjetima obrade)
| Ručno miješanje | |
| Temperatura sirovine ℃ Temperatura kalupa ℃ CT S GT S TFT S Slobodna gustoća kg/m3 | 20-25 Ambijentalna temperatura (15-45 ℃) 35-60 140-200 240-360 28-35 |
Pjenačke izvedbe
| Artikal | Testni standard | Specifikacija |
| Ukupna gustoća kalupa Gustoća jezgre za oblikovanje | ASTM D1622 | ≥50kg/m3 ≥40kg/m |
| Stopa zatvorenih stanica | ASTM D2856 | ≥90% |
| Početna toplinska vodljivost （15 ℃） | ASTM C518 | ≤24MW/(MK) |
| Tlačna čvrstoća | ASTM D1621 | ≥150KPA |
| Dimenzijska stabilnost 24h -20 ℃ RH90 70 ℃ | ASTM D2126 | ≤1% ≤1,5% |
| Brzina apsorpcije vode | ASTM D2842 | ≤3% |