Polyether/TDI nau'in prepolymer

Takaitaccen Bayani:


  • Farashin FOB:US $0.5 - 9,999 / yanki
  • Yawan Oda Min.Guda 100/Kashi
  • Ikon bayarwa:10000 Pieces/Perces per month
  • ƙasar asali:China
  • alamar kasuwanci:INOV
  • Cikakken Bayani

    Tags samfurin

    Samfuran suna da tsayayyar lalacewa mai kyau, juriya na ruwa, juriya na mold, kyawawan kayan aikin injiniya, kuma ana iya ƙara launi don daidaita launi.Ana amfani da shi don yin samfuran polyurethane kamar sandar roba, dabaran roba, faranti, murfin roba da sassa daban-daban.

    Samfura

    D1140

    D1145

    D1155

    D1160

    D1180

    D1185

    NCO/%

    4.0± 0.2

    4.5± 0.2

    5.5± 0.2

    6.0± 0.2

    8.0± 0.2

    8.5± 0.2

    Jihar a 20 ℃

    Ruwan Mai Fassara mara launi

    MOCA100 g prepolymer / g

    11.5

    13.0

    16.0

    17.5

    23

    24.0

    Dankowa (85 ℃)/mPa·s

    340

    300

    250

    250

    450

    400

    Haɗin zafin jiki / ℃ (Prepolymer / MOCA)

    80/120

    80/120

    80/120

    80/120

    75/110

    75/110

    Lokacin gel / min

    10

    9.5

    9

    6

    2

    2

    Lokacin vulcanization (100 ℃) /h

    10

    10

    10

    10

    10

    10

    Hardness ( Shore A)

    78±2

    82±2

    88±1

    92±1

     

     

    Hardness ( Shore D )

     

     

     

     

    70± 1

    78±1

    100% Modulus/MPa

    4.6

    5.0

    5.5

    6.2

    23.2

    32.5

    300% Modul / MPa

    8.2

    9.2

    13.0

    20.8

    -

    -

    Ƙarfin ƙarfi /MPa

    27

    28

    32

    35

    39

    42

    Tsawaita / %

    550

    480

    400

    350

    230

    180

    Ƙarfin hawaye / (KN/m)

    46

    55

    76

    78

    123

    145

    Maimaitawa / %

    28

    24

    24

    33

    40

    51

    Yawan yawa (24℃)/(g/cm3)

    1.11

    1.12

    1.14

    1.14

    1.18

    1.18

    Din wear /mm³

    148

    112

    109

    141

    131

    89

     

    Samfura

    D1230

    D1235

    D1240

    D1245

    D1250

    D1262

    D1265

    D1270

    NCO/%

    3.0± 0.1

    3.5 ± 0.1

    4.0± 0.1

    4.5± 0.2

    5.0± 0.2

    6.2 ± 0.2

    6.5± 0.2

    7.0± 0.2

    Jihar a 20 ℃

    Ruwan Mai Fassara mara launi

    MOCA

    100 g prepolymer / g

    8.6

    10.3

    11.5

    13

    14.5

    18

    19

    20.5

    Dankowa (85 ℃)/mPa·s

    200

    250

    350

    400

    450

    240

    300

    400

    Haɗin zafin jiki / ℃ (Prepolymer / MOCA)

    85/120

    85/120

    80/120

    80/120

    80/120

    75/120

    75/120

    75/120

    Lokacin gel / min

    9

    5

    4.5

    4

    3.5

    3

    2.5

    2

    Lokacin vulcanization (100 ℃) /h

    10

    10

    10

    10

    10

    10

    10

    10

    Hardness ( Shore A)

    70± 2

    78±2

    84±2

    86±2

    90± 1

    94±1

    97 ± 1 (53D)

    60D± 1

    100% Modulus/MPa

    2.1

    4.2

    5.4

    5.9

    8.9

    9.2

    15.2

    15.8

    300% Modul / MPa

    3.0

    6.3

    10.0

    10.3

    14.6

    16.8

    24.6

    23

    Ƙarfin ƙarfi /MPa

    7

    10

    19

    21

    31

    32

    35

    33

    Tsawaita / %

    600

    550

    500

    480

    460

    450

    440

    420

    Ƙarfin hawaye / (KN/m)

    34

    44

    53

    57

    73

    78

    95

    120

    Maimaitawa / %

    50

    48

    41

    31

    30

    31

    41

    43

    Yawan yawa (24℃)/(g/cm3)

    1.08

    1.09

    1.11

    1.13

    1.14

    1.15

    1.16

    1.17

    Din wear /mm³

    163

    159

    116

    157

    135

    117

    143

    135.6