High quality Very first,and Consumer Supreme is our guideline to offer the most beneficial service to our consumers.At present, we're attempting our greatest to be among the top exporters in our area to fulfill buyers far more need to have for Case Series Case, Pu Insole System Material, Pu Shoe-Sole Material Footwear Foam System, We welcome all of the purchasers and pals to contact us for mutual added benefits. Hope to do additional business enterprise along with you.

Good Quality Pu Shoe-Sole Material Footwear Foam System - Pu Safety Shoe Sole System – INOV Detail:

Pu Safety Shoe Sole System

INTRODUCTION

PU Safety shoe-sole system is used to make safety shoe outsoles and inner soles. It is polyester-based PU system material, consist of four components, polyol, ISO, hardner and catalyst. The processing of the system is two components. The catalyst, harder, blowing agent and pigment should be mixed thoroughly with the polyol component EXD-3270A, then mix with ISO component EXD-3119B for making final wares.

PHYSICAL PROPERTIES

A, Inner soles of safety shoe-sole preparing method:

Items	EXD-3270A	EXD-3119B
Ratio（weight ratio）	100	85~88
Material temperature（℃）	45~50	45~50
Rise time（s）	5~7
Tack free time（s）	30~50
Free foam density （g/cm³）	0.35~0.4
Mould temperature（℃）	45~55
Product density（g/cm³）	0.5~0.55
Hardness（Shore A）	55~65
Demould time（min）	3
Elongation at break （%）	≥550
Tear strength（KN/m）	≥22
Tensile strength （MPa）	≥6.0
Ross flexing room temperature	50,000 times no crack

B, Outsoles of safety shoe-sole preparing method:

Items	EXD-3270A	EXD-3119B
Ratio（weight ratio）	100	82~85
Material temperature（℃）	45~50	45~50
Rise time（s）	5~7
Tack free time（s）	30~50
Free foam density （g/cm³）	0.55~0.6
Mould temperature（℃）	45~55
Product density（g/cm³）	0.6~0.8
Hardness（Shore A）	65~75
Demould time（min）	3
Elongation at break （%）	≥600
Tear strength（KN/m）	≥28
Tensile strength （MPa）	≥7.3
Ross flexing room temperature	50,000 times no crack
Demould time(min)	3
Product density(g/cm³)	0.2~0.3
Hardness(Shore C)	30~40
Tensile strength(MPa)	0.45-0.50
Tear strength(KN/m)	2.50-2.60
Elongation(%)	280-300

Product detail pictures:

Related Product Guide:

We strive for excellence, services the customers", hopes to be the top cooperation team and dominator business for personnel, suppliers and prospects, realizes benefit share and continual promotion for Good Quality Pu Shoe-Sole Material Footwear Foam System - Pu Safety Shoe Sole System – INOV , The product will supply to all over the world, such as: Rotterdam, France, Egypt, Our well-equipped facilities and excellent quality control throughout all stages of production enable us to guarantee total customer satisfaction. If you are interested in any of our products or would like to discuss a custom order, please feel free to contact me. We are looking forward to forming successful business relationship with new clients around the world.

Eda Base Eda

Mobile Cover

Polyurethane

Pre-Polymer

We have been cooperated with this company for many years, the company always ensure timely delivery ,good quality and correct number, we are good partners.