Generally customer-oriented, and it's our ultimate goal for being not only the most trusted, trustable and honest provider, but also the partner for our customers for Sealant, Polyurethane Wheels, Block Foam, We are able to do your tailored get to fulfill your own satisfactory! Our organization sets up several departments, including manufacturing department, sales department, high quality control department and sevice center, etc.

Good Quality Pu Shoe-Sole Material Footwear Foam System - Pu Safety Shoe Sole System – INOV Detail:

Pu Safety Shoe Sole System

INTRODUCTION

PU Safety shoe-sole system is used to make safety shoe outsoles and inner soles. It is polyester-based PU system material, consist of four components, polyol, ISO, hardner and catalyst. The processing of the system is two components. The catalyst, harder, blowing agent and pigment should be mixed thoroughly with the polyol component EXD-3270A, then mix with ISO component EXD-3119B for making final wares.

PHYSICAL PROPERTIES

A, Inner soles of safety shoe-sole preparing method:

Items	EXD-3270A	EXD-3119B
Ratio（weight ratio）	100	85~88
Material temperature（℃）	45~50	45~50
Rise time（s）	5~7
Tack free time（s）	30~50
Free foam density （g/cm³）	0.35~0.4
Mould temperature（℃）	45~55
Product density（g/cm³）	0.5~0.55
Hardness（Shore A）	55~65
Demould time（min）	3
Elongation at break （%）	≥550
Tear strength（KN/m）	≥22
Tensile strength （MPa）	≥6.0
Ross flexing room temperature	50,000 times no crack

B, Outsoles of safety shoe-sole preparing method:

Items	EXD-3270A	EXD-3119B
Ratio（weight ratio）	100	82~85
Material temperature（℃）	45~50	45~50
Rise time（s）	5~7
Tack free time（s）	30~50
Free foam density （g/cm³）	0.55~0.6
Mould temperature（℃）	45~55
Product density（g/cm³）	0.6~0.8
Hardness（Shore A）	65~75
Demould time（min）	3
Elongation at break （%）	≥600
Tear strength（KN/m）	≥28
Tensile strength （MPa）	≥7.3
Ross flexing room temperature	50,000 times no crack
Demould time(min)	3
Product density(g/cm³)	0.2~0.3
Hardness(Shore C)	30~40
Tensile strength(MPa)	0.45-0.50
Tear strength(KN/m)	2.50-2.60
Elongation(%)	280-300

Product detail pictures:

Related Product Guide:

We keep on with the basic principle of "quality to start with, support very first, continuous improvement and innovation to meet the customers" for your management and "zero defect, zero complaints" as the quality objective. To great our service, we offer the items with all the superior top quality at the reasonable selling price for Good Quality Pu Shoe-Sole Material Footwear Foam System - Pu Safety Shoe Sole System – INOV , The product will supply to all over the world, such as: Sheffield, Cyprus, Guinea, We are sincerely looking forward to cooperate with customers all over the world. We believe we can satisfy you with our high-quality products and perfect service . We also warmly welcome customers to visit our company and purchase our products.

Eda Base Eda

Elastic Tape

Hockey Court

Ppg2000 2000

Hope that the company could stick to the enterprise spirit of "Quality, Efficiency, Innovation and Integrity", it will be better and better in the future.