MS-930 Silicon Modified sealant
INTRODUCTION
MS-930 is a high performance, neutral single-component sealant based on MS polymer.It reacts with water to form an elastic material, and its tack free time and curing time are related to temperature and humidity.Increasing temperature and humidity can reduce tack free time and curing time, while low temperature and low humidity can also delay this process.
MS-930 has the comprehensive performance of elastic seal and adhesion.It is suitable for the parts that need elastic sealing in addition with certain adhesive strength.
MS-930 is odorless, solvent-free, isocyanate free and PVC free .It has good adhesion to many substances and does not require a primer, which is also suitable for spray-painted surface.This product has been proven to have excellent UV resistance, so it can be used both indoors and outdoors.
FEATURES
A) No formaldehyde, no solvent, no peculiar smell
B) No silicone oil, no corrosion and no pollution to the substrate, environment-friendly
C) Good adhesion of a variety of substances without primer
D) Good mechanical property
E) Stable color, good UV resistance
F) Single component, easy to construct
G) Can be painted
APPLICATION
Industry manufacturing, such as car assembling, ship manufacturing, train body manufacturing ,container metal structure.
Ms-930 has good adhesion to most materials: such as aluminum (polished, anodized), brass, steel, stainless steel, glass, ABS, hard PVC and most thermoplastic materials. The film release agent on the plastic must be removed before adhesion.
Important note: PE, PP, PTFE does not stick to the relay, the material mentioned above is not recommended to test first.
The pretreatment substrate surface must be clean, dry and grease-free.
TECHNICAL INDEX
|
Color |
White/Black/Gray |
|
Odour |
N/A |
|
Status |
Thixotropy |
|
Density |
1.49g/cm3 |
|
Solid content |
100% |
|
Curing mechanism |
Moisture curing |
|
Surface dry time |
≤ 30min* |
|
Curing rate |
4mm/24h* |
|
Tensile strength |
≥3.0 MPa |
|
Elongation |
≥ 150% |
|
Operating temperature |
-40℃ to 100℃ |
* Standard conditions: temperature 23 + 2 ℃,Relative humidity 50±5%
METHOD OF APPLICATION
The corresponding manual or pneumatic glue gun should be used for soft packaging, and it is recommended to control within 0.2-0.4mpa when pneumatic glue gun is used. Too low temperature will lead to increased viscosity, it is recommended to preheat sealants at room temperature before application.
COATING PERFORMANCE
Ms-930 can be painted, however, adaptability tests are recommended for a wide variety of paints.
STORAGE
Storage temperature: 5 ℃ to 30 ℃
Storage time: 9 months in the original packaging.
Product detail pictures:
Related Product Guide:
Our commission is to serve our users and clients with best quality and competitive portable digital products for Good quality Pu Foam Insole System Material - MS-930 Silicon Modified sealant – INOV , The product will supply to all over the world, such as: Singapore, Turkmenistan, Portugal, Our product quality is one of the major concerns and has been produced to meet the customer's standards. "Customer services and relationship" is another important area which we understand good communication and relationships with our customers is the most significant power to run it as a long term business.
By Judy from Curacao - 2017.05.02 11:33
The customer service reprersentative explained very detailed, service attitude is very good, reply is very timely and comprehensive, a happy communication! We hope to have a opportunity to cooperate.
By Diana from Vancouver - 2018.05.22 12:13