Good Quality Polyurethane Elastomers - Quasi MDI-terminated system – INOV
Good Quality Polyurethane Elastomers - Quasi MDI-terminated system – INOV Detail:
Quasi MDI-terminated PTMG system
DESCRIPTION
Component: DY2513 is consist by Components ABC. Component A is polyol, B is polyurethane prepolymer which ended up with isocynate, C is chain extender.
Characteristic: The final product enjoys good anti resistance ability, good rebound. And the hardness can be adjusted by the different ratio. The color can be adjusted by pigment.
Application: This material was used to produce Polyurethane sieves, PU rollers, cleaning pigs (discs) and other elastomer.
SPECIFICATION
|
Type |
DY2513-B |
DY2513-A |
DY2513-C |
|||||
|
NCO/% |
13.1 |
|
|
|||||
|
Operation temperature /℃ |
45 |
50 |
45 |
|||||
|
Viscosity mPa·s/ |
800 |
1200 |
30 |
|||||
|
Prepolymer |
DY2513-B |
|||||||
|
Chain extender |
DY2513-A﹢DY2513-C |
|||||||
|
Hardness /shore A |
60 |
65 |
70 |
75 |
80 |
85 |
90 |
95 |
|
DY2513-B（ratio, by weight ） |
100 |
100 |
100 |
100 |
100 |
100 |
100 |
100 |
|
DY2513-A（ratio, by weight ） |
180 |
150 |
120 |
100 |
80 |
60 |
40 |
20 |
|
DY2513-C（ratio, by wight） |
5.7 |
7 |
8.4 |
9.3 |
10.2 |
11.1 |
12 |
12.9 |
|
Catalyst/total amount A+B+C % |
0.6 |
0.6 |
0.6 |
0.45 |
0.3 |
0.3 |
0.24 |
0.24 |
|
Mold temperature/℃ |
100 |
|||||||
|
Gel time/min |
2，30 |
2，30 |
2，20 |
2，20 |
2，30 |
2，30 |
2，10 |
2，10 |
|
Open Mold Time/ min |
60 |
50 |
40 |
40 |
40 |
40 |
40 |
40 |
Quasi MDI-terminated Polyester system
DESCRIPTION
It is used to produce Polyurethane sieves, PU rollers and other elastomer. It should be processed by mid-temperature casting machine.
The final product enjoys good anti resistance ability, good rebound. And the hardness can be adjusted by the different ratio. The color can be adjusted by pigment.
Application: automotive kits, pipe cleaners, etc., polyurethane large or small product components.
SPECIFICATION
|
Type |
DY3516-B |
DY3516-A |
DY3516-C |
|||||||
|
NCO/% |
16.5±0.2 |
|
|
|||||||
| Operation temperature /℃ |
45 |
70 |
45 |
|||||||
|
Viscosity mPa·s/ |
700 |
730 |
30 |
|||||||
|
Prepolymer |
DY3516-B |
|||||||||
|
Chain extender |
DY3516-A+DY3516-C |
|||||||||
|
Hardness /shore A |
55 |
60 |
65 |
70 |
75 |
80 |
85 |
90 |
||
|
DY3516-B(ratio, by weight） |
100 |
100 |
100 |
100 |
100 |
100 |
100 |
100 |
||
|
DY3516-A(ratio, by weight） |
380 |
180 |
160 |
130 |
110 |
100 |
80 |
60 |
||
| DY3516-C(ratio, by weight) |
0 |
9.1 |
10 |
11.4 |
12.3 |
12.7 |
13.6 |
14.5 |
||
|
Catalyst/total amount A+B+C % |
0.4 |
0.4 |
0.4 |
0.4 |
0.3 |
0.3 |
0.3 |
0.3 |
||
|
Mold temperature/℃ |
100 |
|||||||||
|
Gel time/min |
5 |
5 |
5 |
5 |
5 |
4 |
4 |
4 |
||
|
Open Mold Time/ min |
50 |
35 |
35 |
30 |
30 |
30 |
30 |
30 |
||
|
Post cure time(90℃)/h |
16 |
|||||||||
AUTOMATIC CONTROL
The production is controlled by DCS system, and packing by automatic filling machine. Package is 200KG/DRUM Or 20KG/DRUM.
Product detail pictures:
Related Product Guide:
Fast and very good quotations, informed advisers to help you choose the correct merchandise that suits all your preferences, a short creation time, responsible excellent command and different companies for paying and shipping affairs for Good Quality Polyurethane Elastomers - Quasi MDI-terminated system – INOV , The product will supply to all over the world, such as: United States, Juventus, Greenland, Our solutions are produced with the best raw materials. Every moment, we constantly improve the production programme. In order to ensure better quality and service, we now have been focusing on the production process. We have got high praise by partner. We are looking forward to establishing business relationship with you.
By Alexandra from Curacao - 2018.11.04 10:32
Timely delivery, strict implementation of the contract provisions of the goods, encountered special circumstances, but also actively cooperate, a trustworthy company!
By Grace from Seattle - 2018.06.19 10:42