Réamhpholaiméir de chineál polyether/TDI
Tá friotaíocht caitheamh maith ag na táirgí, friotaíocht uisce, friotaíocht múnla, airíonna meicniúla den scoth, agus is féidir dath a chur leis chun an dath a choigeartú.Úsáidtear é chun táirgí polúireatán a dhéanamh ar nós bata rubair, roth rubair, pláta, sciath rubair agus páirteanna ilghnéitheacha.
| Mionsamhail | D1140 | D1145 | D1155 | D1160 | D1180 | D1185 |
| NCO/% | 4.0±0.2 | 4.5±0.2 | 5.5±0.2 | 6.0±0.2 | 8.0±0.2 | 8.5±0.2 |
| Luaigh ag 20 ℃ | Leacht Trédhearcach Gan Dath | |||||
| MOCA100g Réamhpholaiméir /g | 11.5 | 13.0 | 16.0 | 17.5 | 23 | 24.0 |
| Slaodacht (85 ℃)/mPa·s | 340 | 300 | 250 | 250 | 450 | 400 |
| Teocht a mheascadh / ℃ （Prepolymer / MOCA） | 80/120 | 80/120 | 80/120 | 80/120 | 75/110 | 75/110 |
| Am glóthach / nóim | 10 | 9.5 | 9 | 6 | 2 | 2 |
| Am iar-bholcánaithe (100 ℃) / h | 10 | 10 | 10 | 10 | 10 | 10 |
| Cruas （Cladach A） | 78±2 | 82±2 | 88±1 | 92±1 |
|
|
| Cruas （Cladach D） |
|
|
|
| 70±1 | 78±1 |
| 100% Modal/MPa | 4.6 | 5.0 | 5.5 | 6.2 | 23.2 | 32.5 |
| 300% Modal /MPa | 8.2 | 9.2 | 13.0 | 20.8 | - | - |
| Neart teanntachta /MPa | 27 | 28 | 32 | 35 | 39 | 42 |
| Fadú / % | 550 | 480 | 400 | 350 | 230 | 180 |
| Neart cuimilt / （KN/m） | 46 | 55 | 76 | 78 | 123 | 145 |
| Rebound / % | 28 | 24 | 24 | 33 | 40 | 51 |
| Dlús (24 ℃)/（g/ cm3） | 1. 11 | 1.12 | 1.14 | 1.14 | 1. 18 | 1. 18 |
| Caith /mm³ | 148 | 112 | 109 | 141 | 131 | 89 |
| Mionsamhail | D1230 | D1235 | D1240 | D1245 | D1250 | D1262 | D1265 | D1270 |
| NCO/% | 3.0±0.1 | 3.5±0.1 | 4.0±0.1 | 4.5±0.2 | 5.0±0.2 | 6.2±0.2 | 6.5±0.2 | 7.0±0.2 |
| Luaigh ag 20 ℃ | Leacht Trédhearcach Gan Dath | |||||||
| MOCA 100g Réamhpholaiméir /g | 8.6 | 10.3 | 11.5 | 13 | 14.5 | 18 | 19 | 20.5 |
| Slaodacht (85 ℃)/mPa·s | 200 | 250 | 350 | 400 | 450 | 240 | 300 | 400 |
| Teocht a mheascadh / ℃ （Prepolymer / MOCA） | 85/120 | 85/120 | 80/120 | 80/120 | 80/120 | 75/120 | 75/120 | 75/120 |
| Am glóthach / nóim | 9 | 5 | 4.5 | 4 | 3.5 | 3 | 2.5 | 2 |
| Am iar-bholcánaithe (100 ℃) / h | 10 | 10 | 10 | 10 | 10 | 10 | 10 | 10 |
| Cruas （Cladach A） | 70±2 | 78±2 | 84±2 | 86±2 | 90±1 | 94±1 | 97±1（53d） | 60D±1 |
| 100% Modal/MPa | 2.1 | 4.2 | 5.4 | 5.9 | 8.9 | 9.2 | 15.2 | 15.8 |
| 300% Modal /MPa | 3.0 | 6.3 | 10.0 | 10.3 | 14.6 | 16.8 | 24.6 | 23 |
| Neart teanntachta /MPa | 7 | 10 | 19 | 21 | 31 | 32 | 35 | 33 |
| Fadú / % | 600 | 550 | 500 | 480 | 460 | 450 | 440 | 420 |
| Neart cuimilt / （KN/m） | 34 | 44 | 53 | 57 | 73 | 78 | 95 | 120 |
| Rebound / % | 50 | 48 | 41 | 31 | 30 | 31 | 41 | 43 |
| Dlús (24 ℃)/（g/ cm3） | 1. 08 | 1. 09 | 1. 11 | 1.13 | 1.14 | 1.15 | 1. 16 | 1. 17 |
| Caith /mm³ | 163 | 159 | 116 | 157 | 135 | 117 | 143 | 135.6 |