Donfoam 812 HCFC-141B base blend polyols for block foam
Donfoam 812 HCFC-141B base blend polyols for block foam
INTRODUCTION
Donfoam 812 blend polyether polyols used for produce PUR block foam. The foam has uniform cell , low thermal conductivity, thermal insulation performance is good, flame retardant performance is good, low temperature no shrinking crack etc.
Widely used in the process of all kinds of insulation work such as: building external wall, cold storage, tanks, large pipes etc.
PHYSICAL PROPERTY
| Appearance
Dynamic viscosity （25℃） mPa.S Density （20℃） g/ml Storage temperature ℃ Storage stability month |
Light yellow to brown transparent liquid 250±50 1.17±0.1 10-25 6 |
RECOMMENDED RATIO
| Items |
PBW |
| Blend Polyether Polyol
Isocyanate |
100 130 |
TECHNOLOGY AND REACTIVITY (the exact value varies depending on processing conditions)
|
Manual Mixing |
|
| Raw Material Temperature ℃
Mould Temperature ℃ CT s GT s TFT s Free Density kg/m3 |
20-25 Ambient Temperature(15-45℃ ) 35-60 140-180 240-260 26-28 |
FOAM PERFORMANCES
|
Item |
Test Standard |
Specification |
| Overall Molding Density
Molding Core Density |
GB 6343 |
40-45kg/m3 38-42kg/m |
| Closed-cell Rate |
GB 10799 |
≥90% |
| Initial Thermal Conductivity（15℃） |
GB 3399 |
≤24mW/(m.K) |
| Compressive Strength |
GB/T8813 |
≥150kPa |
| Dimensional Stability
24h -20℃ RH90 70℃ |
GB/T8811 |
≤1% ≤1.5% |
| Water Absorption Rate |
GB 8810 |
≤3% |
| Flammability |
ASTM E84 |
Class A |