"Sincerity, Innovation, Rigorousness, and Efficiency" could be the persistent conception of our organization for your long-term to establish alongside one another with shoppers for mutual reciprocity and mutual benefit for Polymer Polyol, Block Foam& Pouring, Playground Surface, We welcome new and previous customers from all walks of lifetime to speak to us for future organization relationships and mutual achievement!

2019 China New Design Ppg1000 1000 - Pu Safety Shoe Sole System – INOV Detail:

Pu Safety Shoe Sole System

INTRODUCTION

PU Safety shoe-sole system is used to make safety shoe outsoles and inner soles. It is polyester-based PU system material, consist of four components, polyol, ISO, hardner and catalyst. The processing of the system is two components. The catalyst, harder, blowing agent and pigment should be mixed thoroughly with the polyol component EXD-3270A, then mix with ISO component EXD-3119B for making final wares.

PHYSICAL PROPERTIES

A, Inner soles of safety shoe-sole preparing method:

Items	EXD-3270A	EXD-3119B
Ratio（weight ratio）	100	85~88
Material temperature（℃）	45~50	45~50
Rise time（s）	5~7
Tack free time（s）	30~50
Free foam density （g/cm³）	0.35~0.4
Mould temperature（℃）	45~55
Product density（g/cm³）	0.5~0.55
Hardness（Shore A）	55~65
Demould time（min）	3
Elongation at break （%）	≥550
Tear strength（KN/m）	≥22
Tensile strength （MPa）	≥6.0
Ross flexing room temperature	50,000 times no crack

B, Outsoles of safety shoe-sole preparing method:

Items	EXD-3270A	EXD-3119B
Ratio（weight ratio）	100	82~85
Material temperature（℃）	45~50	45~50
Rise time（s）	5~7
Tack free time（s）	30~50
Free foam density （g/cm³）	0.55~0.6
Mould temperature（℃）	45~55
Product density（g/cm³）	0.6~0.8
Hardness（Shore A）	65~75
Demould time（min）	3
Elongation at break （%）	≥600
Tear strength（KN/m）	≥28
Tensile strength （MPa）	≥7.3
Ross flexing room temperature	50,000 times no crack
Demould time(min)	3
Product density(g/cm³)	0.2~0.3
Hardness(Shore C)	30~40
Tensile strength(MPa)	0.45-0.50
Tear strength(KN/m)	2.50-2.60
Elongation(%)	280-300

Product detail pictures:

Related Product Guide:

Our merchandise are commonly recognized and reliable by customers and can meet constantly developing economic and social desires for 2019 China New Design Ppg1000 1000 - Pu Safety Shoe Sole System – INOV , The product will supply to all over the world, such as: Georgia, Surabaya, Iran, Our company is an international supplier on this kind of merchandise. We supply an amazing selection of high-quality merchandise. Our goal is to delight you with our distinctive collection of mindful items while providing value and excellent service. Our mission is simple: To supply the best items and service to our customers at the lowest prices possible.